上海斯米克S223无硅锡黄铜焊丝 

Category

类别

Trade

mark

牌号

Chemical composition

主要成份()

Characteristics & application

特性和用途

Equivalent to AWS

相当AWS

 

Hardfacing

 

硬

 

面

 

栈

 

焊

S 101

C3 Cr28 Ni4

Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.

HRc48-54，耐磨、耐气蚀、抗氧化。栈焊铲斗齿，泵套

 

S 111

C1 Cr29 W5

Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.

HRc38-47，高温下耐磨、耐蚀。栈焊高温高压阀门

ECoCr-A

S 112

C1.5 Cr29 W8

Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.

HRc45-50，高温下耐磨、耐蚀。栈焊阀门，热轧孔型

ECoCr-B

S 113

C2.5 Cr30 W17

Co Rem.

HRc55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.

HRc55，高温下耐磨、耐热，但抗冲击性差。栈焊螺旋送料机用

 

S 114

C2.5 Cr30 W12

Co Rem.

HRc53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.

HRc53，高温下耐磨、耐热，但抗冲击较差。栈焊牙轮钻头

ECoCr-C

 

Copper

alloys

 

 

铜

 

 

合

 

 

金

S 201

Sn1 Si0.3Mn0.3

Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.

机械性能好，抗裂性好。紫铜气焊及氩弧焊用

ERCu

S 211

Si3 Mn1

Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.

机械性能好，铜合金氩弧焊及钢的MIG钎焊用

ERCuSi-Al

S 212

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨性好。铜合金氩弧焊及钢的栈焊用

ERCuSn-A

S 213

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨性好。铜合金氩弧焊及钢的栈焊用

ERCuSn-C

S 214

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨、耐蚀。铜合金氩弧焊及钢的栈焊用

ERCuAl-A1

S 215

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨、耐蚀。铜合金氩弧焊及钢的栈焊用

ERCuAl-A2

S 221

Cu60 Sn1 Si0.3

Zn Rem.

Melting point is about 890. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔点约890。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

 

S 221F

Cu60 Sn1 Si 0.3

Zn Rem.

S221 welding rod coated with flux.

外涂焊剂的S221焊丝

 

S 222

Cu58Sn0.9Si0.1

Fe0.8 Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔点约880。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-C

S 222F

Cu58Sn0.9Si0.1

Fe0.8 Zn Rem.

S222 welding rod coated with flux.

外涂焊剂的S222焊丝

RBCuZn-C

S 223

Cu59 Sn0.6

Zn Rem.

Melting point is about 900. Braze welding of copper, steel and cast iron.

熔点约900。铜、钢、铸铁钎焊用

上海斯米克S223无硅锡黄铜焊丝 

RBCuZn-A

S 224

Cu62 Si0.5

Zn Rem.

Melting point is about 905. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔点约905。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

 

Copper

alloys

铜

 

合

 

金

S 225

Cu48 Ni10

Zn Rem.

Melting point is about 935and high strength. Braze welding of steel, nickel and carbide alloys.

熔点约935。高强度,钎焊钢、镍及硬质合金用

RBCuZn-D

S 225F

Cu48 Ni10

Zn Rem.

S225 welding rod coated with flux.

外涂焊剂的S225焊丝

RBCuZn-D

S 226

Cu60 Sn0.3

Si0.2 Zn Rem.

Melting point is about 900. Gas welding of brass, also braze welding of copper, steel and cast iron.

熔点约900。黄铜气焊用，也可钎焊铜、钢、铸铁

 

S 227

Cu58Sn0.9Ni0.5

Si0.1 Fe0.8

Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔点880。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-B

S 229

Cu55 Ni6 Mn4

Zn余

Melting point is about 920, high strength. Braze welding of steel, nickel and hard carbide.

熔点约920。高强度,钎焊钢、镍及硬质合金用

 

Aluminum alloys

 

铝

 

合

 

金

S 301

Al99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.

塑性好、耐蚀。纯铝气焊、氩弧焊用

ER1100

S 311

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.

抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金

ER4043

S 321

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.

良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

 

S 331

Mg5 Mn0.4

Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.

耐蚀，强度高。铝合金氩弧焊用

上海斯米克S223无硅锡黄铜焊丝 