PPO 沙伯基础创新塑料（原GE）Sabic WCP781无卤阻燃良好的柔韧性低比重注塑级聚苯醚插头连接器应用

PPO 沙伯基础创新塑料（原GE）Sabic WCP781无卤阻燃良好的柔韧性低比重注塑级聚苯醚插头连接器应用

中文简介：WCP781，柔性注塑级PPE-TPE。低比重，非常好的无卤阻燃性能。适用于二次注塑应用，如插头、应变消除装置和连接器。UL 94-V0性能良好，可加工。邵氏硬度80A。英文简介：WCP781,Flexible PPE-TPE injection grade. Low specific gravity with very good halogen free flame retardant performance. Suitable for overmolding applications such as plugs, strain relief's, and connectors. UL 94-V0 performance with good processability. 80 Shore A hardness.

SABIC Innovative Plastics NORYL WCP781 PPE-TPE 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.08 g/cc	1.08 g/cc	ASTM D792
吸水率	0.23 % @Time 173000 sec	0.23 % @Time 48.0 hour	ASTM D570
线性成型收缩率,Flow	0.0049 cm/cm @Time 86400 sec	0.0049 in/in @Time 24.0 hour	ASTM D955
线性成型收缩率，横向	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ASTM D955
熔体流动速率	13.5 g/10 min @Load 5.00 kg, Temperature 210 °C	13.5 g/10 min @Load 11.0 lb, Temperature 410 °F	ASTM D1238
	17.4 g/10 min @Load 2.16 kg, Temperature 250 °C	17.4 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 A)	80	80	30S reading; ASTM D2240
抗张强度(断裂)	13.0 MPa	1890 psi	Type I, 50 mm/min; ASTM D638
	13.0 MPa	1890 psi	50 mm/min; ISO 527
伸长率 (断裂)	168 %	168 %	50 mm/min; ISO 527
	175 %	175 %	Type I, 50 mm/min; ASTM D638
弯曲模量	0.0600 GPa	8.70 ksi	12.5 mm/min, 100 mm span; ASTM D790
	0.0800 GPa	11.6 ksi	12.5 mm/min; ISO 178
撕裂强度	8.00 kN/m	45.6 pli	ISO 6383

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	3.80e+14 ohm-cm	3.80e+14 ohm-cm	IEC 60093
介电常数	3.1 @Frequency 1.00e+6 Hz	3.1 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 50.0 - 60.0 Hz	3.4 @Frequency 50.0 - 60.0 Hz	IEC 60250
介电强度	22.0 kV/mm @Thickness 2.00 mm	559 kV/in @Thickness 0.0787 in	in oil; IEC 60243-1
耗散因数	0.0020 @Frequency 1.00e+6 Hz	0.0020 @Frequency 1.00e+6 Hz	IEC 60250
	0.0050 @Frequency 50.0 - 60.0 Hz	0.0050 @Frequency 50.0 - 60.0 Hz	IEC 60250
相比耐漏电起痕指数(CTI)	600 V	600 V	IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
脆化温度	<= -40.0 °C	<= -40.0 °F	ASTM D746
可燃性(UL94)	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in	UL 94
极限氧指数	25 %	25 %	ISO 4589
灼热丝试验	725 °C	1340 °F	IEC 60695-2-13
	850 °C @Thickness 3.00 mm	1560 °F @Thickness 0.118 in	IEC 60695-2-12

材料描述		测试方法
Smoke Density on 0.5mm plaque, Flame, Ds, max	142	ASTM E 662
Smoke Density on 0.5mm plaque, Non-flame, Ds, max	84	ASTM E 662

搜好货厂家广东墨澜塑胶有限公司为您提供PPO 沙伯基础创新塑料（原GE）Sabic WCP781无卤阻燃良好的柔韧性低比重注塑级聚苯醚插头连接器应用的详细产品价格、产品图片等产品介绍信息，您可以直接联系厂家获取PPO 沙伯基础创新塑料（原GE）Sabic WCP781无卤阻燃良好的柔韧性低比重注塑级聚苯醚插头连接器应用的具体资料，联系时请说明是在搜好货网看到的。