EXL9330 BK1A068 耐寒-60度 阻燃V0黑色 超韧耐寒 不脆化PC 抗低温脆裂性 零下60度 高韧性PC

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

590

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

620

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

6

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

130

%

ASTM D 638

Tensile Modulus, 50 mm/min

21400

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

900

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

21000

kgf/cm2

ASTM D 790

Tensile Stress, yield, 50 mm/min

55

MPa

ISO 527

Tensile Stress, break, 50 mm/min

60

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

6

%

ISO 527

Tensile Strain, break, 50 mm/min

125

%

ISO 527

Tensile Modulus, 1 mm/min

2100

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

85

MPa

ISO 178

Flexural Modulus, 2 mm/min

2200

MPa

ISO 178

Hardness, H358/30

90

MPa

ISO 2039-1

IMPACT

Izod Impact, notched, 23°C

81

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

69

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -50°C

59

cm-kgf/cm

ASTM D 256

Izod Impact, notched, 23°C, 6.4mm

65

cm-kgf/cm

ASTM D 256

Izod Impact, double-gated, 23°C

108

cm-kgf/cm

SABIC Method

Instrumented Impact Total Energy, 23°C

539

cm-kgf

ASTM D 3763

Izod Impact, unnotched 80*10*3 +23°C

NB

kJ/m2

ISO 180/1U

Izod Impact, unnotched 80*10*3 -30°C

NB

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*3 +23°C

70

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

55

kJ/m2

ISO 180/1A

Izod Impact, notched 63.5*12.7*3.2, 23°C

80

kJ/m2

ISO 180/4A

Izod Impact, notched 63.5*12.7*3.2, -30°C

65

kJ/m2

ISO 180/4A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

75

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

60

kJ/m2

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m2

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m2

ISO 179/1eU

THERMAL

Vicat Softening Temp, Rate B/50

142

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

134

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

120

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

124

°C

ASTM D 648

CTE, -40°C to 40°C, flow

6.66E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.66E-05

1/°C

ASTM E 831

CTE, 23°C to 80°C, flow

7.2E-05

1/°C

ISO 11359-2

CTE, 23°C to 80°C, xflow

7.7E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

-

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

140

°C

ISO 306

Vicat Softening Temp, Rate B/120

142

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

135

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

124

°C

ISO 75/Ae

Relative Temp Index, Elec

125

°C

UL 746B

Relative Temp Index, Mech w/impact

115

°C

UL 746B

Relative Temp Index, Mech w/o impact

120

°C

UL 746B

PHYSICAL

Specific Gravity

1.18

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm

0.4 - 0.8

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm

0.4 - 0.8

%

SABIC Method

Melt Flow Rate, 300°C/1.2 kgf

10

g/10 min

ASTM D 1238

Density

1.19

g/cm2

ISO 1183

Water Absorption, (23°C/sat)

0.35

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.15

%

ISO 62

Melt Volume Rate, MVR at 300°C/1.2 kg

9

cm210 min

ISO 1133

ELECTRICAL

Dielectric Strength, in oil, 3.2 mm

17

kV/mm

ASTM D 149

Relative Permittivity, 50/60 Hz

2.95

-

ASTM D 150

Relative Permittivity, 1 MHz

2.9

-

ASTM D 150

Dissipation Factor, 50/60 Hz

0.0024

-

ASTM D 150

Dissipation Factor, 1 MHz

0.0085

-

ASTM D 150

Hot Wire Ignition {PLC)

1

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC}

3

PLC Code

UL 746A

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 3.2 mm

16

kV/mm

IEC 60243-1

Relative Permittivity, 50/60 Hz

2.6

-

IEC 60250

Relative Permittivity, 1 MHz

2.7

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.001

-

IEC 60250

Dissipation Factor, 1 MHz

0.008

-

IEC 60250

Comparative Tracking Index

225

V

IEC 60112

FLAME CHARACTERISTICS

UL Recognized, 94V-0 Flame Class Rating (3)

1.49

mm

UL 94

UL Recognized, 94-5VA Rating (3)

2.99

mm

UL 94

Glow Wire Flammability Index 960°C, passes at

1

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature, 1.0 mm

825

°C

IEC 60695-2-13

Oxygen Index (LOI)

35

%

ISO 4589

UV-light, water exposure/immersion

F1

-

UL 746C

Injection Molding

Drying Temperature

120

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

48

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

295 - 315

°C

Nozzle Temperature

290 - 310

°C

Front - Zone 3 Temperature

295 - 315

°C

Middle - Zone 2 Temperature

280 - 305

°C

Rear - Zone 1 Temperature

215 - 295

°C

Mold Temperature

70 - 95

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

40 - 60

%

Vent Depth

0.025 - 0.076

mm