瑞典伊萨DUAL SHIELD 9000-B3L低碳钢药芯气保焊丝

Dual Shield 9000-B3L is an all-position flux cored electrode for low carbon grades of 2.25% Cr-1% Mo steels. It is designed for use with 75% - 90% Argon, remainder CO2 shielding gases. The weld metal analysis is similar to an E9018-B3L low hydrogen electrode

Typical Tensile Properties

Condition	Elongation	Tensile Strength	Testing Temperature	Testing Time	Yield Strength
Stress Relieved	22 %	635 MPa (92 ksi)	691 degC (1275 degF)	1 hr	545 MPa (79 ksi)

Deposition Data

Current	Deposition Rate	Diameter	Deposition Efficiency (%)	Voltage	Wire Feed Speed
75% Ar - 25% CO2
450 A	7.3 kg/h (16 lb/h)	1.6 mm (1/16 in.)	87 %	33 V	016 cm/min (400 in./min)
500 A	9.11 kg/h (20.1 lb/h)	1.6 mm (1/16 in.)	87 %	39 V	1270 cm/min (500 in./min)
150 A	1.91 kg/h (4.2 lb/h)	1.2 mm (.045 in.)	86 %	28 V	508 cm/min (200 in./min)
250 A	3.86 kg/h (8.5 lb/h)	1.2 mm (.045 in.)	87 %	30 V	1016 cm/min (400 in./min)
290 A	4.85 kg/h (10.7 lb/h)	1.2 mm (.045 in.)	87 %	33 V	1270 cm/min (500 in./min)
330 A	5.76 kg/h (12.7 lb/h)	1.2 mm (.045 in.)	87 %	34 V	1524 cm/min (600 in./min)
155 A	2 kg/h (4.4 lb/h)	1.4 mm (.052 in.)	87 %	25 V	381 cm/min (150 in./min)
245 A	3.31 kg/h (7.3 lb/h)	1.4 mm (.052 in.)	86 %	28 V	635 cm/min (250 in./min)
310 A	4.63 kg/h (10.2 lb/h)	1.4 mm (.052 in.)	85 %	33 V	889 cm/min (350 in./min)
360 A	6.03 kg/h (13.3 lb/h)	1.4 mm (.052 in.)	85 %	36 V	1143 cm/min (450 in./min)
430 A	7.98 kg/h (17.6 lb/h)	1.4 mm (.052 in.)	87 %	37 V	1524 cm/min (600 in./min)
190 A	2.77 kg/h (6.1 lb/h)	1.6 mm (1/16 in.)	87 %	27 V	38 cm/min (150 in./min)
300 A	4.63 kg/h (10.2 lb/h)	1.6 mm (1/16 in.)	87 %	30 V	35 cm/min (250 in./min)
365 A	5.58 kg/h (12.3 lb/h)	1.6 mm (1/16 in.)	86 %	33 V	762 cm/min (300 in./min)
410 A	6.35 kg/h (14 lb/h)	1.6 mm (1/16 in.)	88 %	33 V	889 cm/min (350 in./min)
210 A	2.86 kg/h (6.3 lb/h)	1.2 mm (.045 in.)	86 %	29 V	762 cm/min (300 in./min)

Classifications

Classifications

ASME SFA 5.36 :ASME SFA 5.29 :AWS A5.36 : E91Ti-C1PZ-B3LAWS A5.36 : E91T1-M21PZ-B3LAWS A5.29 : E91T1-B3LC/B3LM

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C	Cr	Mn	Mo	P	S	Si
75% Ar - 25% CO2
0.02 %	2.20 %	0.80 %	1.10 %	0.01 %	0.01 %	0.40 %

搜好货厂家赫克托（上海）焊材有限公司为您提供瑞典伊萨DUAL SHIELD 9000-B3L低碳钢药芯气保焊丝的详细产品价格、产品图片等产品介绍信息，您可以直接联系厂家获取瑞典伊萨DUAL SHIELD 9000-B3L低碳钢药芯气保焊丝的具体资料，联系时请说明是在搜好货网看到的。