Dual Shield 8000-B2L is an all-position flux cored electrode for low carbon grades of 1.25% Cr - 0.5% Mo steels. It is designed for use with 75% - 90% Argon, remainder CO2 shielding gases. The weld metal analysis is similar to an E8018-B2L low Hydrogen electrode.
| Condition | Elongation | Shielding Gas | Tensile Strength | Testing Temperature | Testing Time | Yield Strength |
| Stress Relieved | 23 % | 75% Ar - 25% CO2 | 605 MPa (87 ksi) | 691 degC (1275 degF) | 1 hr | 525 MPa (76 ksi) |
| Current | Deposition Rate | Diameter | Deposition Efficiency (%) | Voltage | Wire Feed Speed |
| 190 A | 2.77 kg/h (6.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 27 V | 38 cm/min (150 in./min) |
| 300 A | 4.63 kg/h (10.2 lb/h) | 1.6 mm (1/16 in.) | 87 % | 30 V | 35 cm/min (250 in./min) |
| 365 A | 5.58 kg/h (12.3 lb/h) | 1.6 mm (1/16 in.) | 86 % | 33 V | 762 cm/min (300 in./min) |
| 410 A | 6.35 kg/h (14 lb/h) | 1.6 mm (1/16 in.) | 88 % | 33 V | 889 cm/min (350 in./min) |
| 450 A | 7.3 kg/h (16 lb/h) | 1.6 mm (1/16 in.) | 87 % | 33 V | 1016 cm/min (400 in./min) |
| 500 A | 9.11 kg/h (20.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 39 V | 1270 cm/min (500 in./min) |
| 150 A | 1.91 kg/h (4.2 lb/h) | 1.2 mm (.045 in.) | 86 % | 28 V | 508 cm/min (200 in./min) |
| 210 A | 86 kg/h (6.3 lb/h) | 1.2 mm (.045 in.) | 86 % | 29 V | 762 cm/min (300 in./min) |
| 250 A | 3.86 kg/h (8.5 lb/h) | 1.2 mm (.045 in.) | 87 % | 30 V | 1016 cm/min (400 in./min) |
| 290 A | 4.85 kg/h (10.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 33 V | 1270 cm/min (500 in./min) |
| 330 A | 5.76 kg/h (12.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 34 V | 1524 cm/min (600 in./min) |
| 155 A | 2 kg/h (4.4 lb/h) | 1.4 mm (.052 in.) | 87 % | 25 V | 381 cm/min (150 in./min) |
| 245 A | 3.31 kg/h (7.3 lb/h) | 1.4 mm (.052 in.) | 86 % | 28 V | 635 cm/min (250 in./min) |
| 310 A | 4.63 kg/h (10.2 lb/h) | 1.4 mm (.052 in.) | 85 % | 33 V | 889 cm/min (350 in./min) |
| 360 A | 6.03 kg/h (13.3 lb/h) | 1.4 mm (.052 in.) | 85 % | 36 V | 1143 cm/min (450 in./min) |
| 430 A | 7.98 kg/h (17.6 lb/h) | 1.4 mm (.052 in.) | 87 % | 37 V | 1524 cm/min (600 in./min) |
| Classifications | ASME SFA 5.36 :ASME SFA 5.29 :AWS A5.36 : E81T1-M21PZ-B2LAWS A5.29 : E81T1-B2LM |
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Cr | Mn | Mo | P | S | Si | ||||||||
| 75% Ar - 25% CO2 | ||||||||||||||
| 0.02 % | 1.40 % | 0.90 % | 0.50 % | 0.010 % | 0.010 % | 0.40 % | ||||||||
搜好货厂家赫克托（上海）焊材有限公司为您提供伊萨合金钢药芯焊丝DUAL SHIELD 8000-B2L碳钢气保焊丝的详细产品价格、产品图片等产品介绍信息，您可以直接联系厂家获取伊萨合金钢药芯焊丝DUAL SHIELD 8000-B2L碳钢气保焊丝的具体资料，联系时请说明是在搜好货网看到的。
| 品牌 : | 伊萨 |
| 型号 : | SHIELD 8000-B2L |
| 产地 : | 瑞典 |
| 类型 : | 药芯 |
| 材质 : | 合金 |
| 助焊剂含量 : | 1 |
| 加工定制 : | 否 |
| 焊丝直径 : | 1.2-1.6 |
| 熔点 : | 240 |
| 长度 : | 盘装 |
| 重量 : | 15公斤/盘 |
| 工作温度 : | 120-180 |
| 焊接电流 : | 180 |
| 是否含助焊剂 : | 否 |
| 适用范围 : | 广泛 |
联 系 人
联系电话
采购说明