Dual Shield II 101H4M is one of a series of low hydrogen flux cored electrodes introduced by ESAB. Each of the new Dual Shield II H4 wires is an all-position flux cored electrode that provides excellent low temperature toughness in both the as welded and/or stress relieved conditions (as applicable) when used with 75% Ar/25% CO2. Each can produce diffusible hydrogen levels of < 4mL/100g deposited over a wide range of welding parameters. Dual Shield II 101H4M is especially designed to weld HY-80 and HSLA-100 steels typically used in shipbuilding. Suitable for single or multi-pass welding applications. This wire was developed to meet the stringent requirements of MIL-E-24403/2 and offshore welding, and it is an ideal choice for HSLA steels.
As Welded 75% Ar - 25% Co2 |
Condition | As Welded | As Welded |
AWS A5.29 Requirement | MIL-E-24403/2 Vertical-Up HY-80 Base Plate | |
Reduction in Area | 67 % | 68 % |
Shielding Gas | 75% Ar - 25% CO2 | 75% Ar - 25% CO2 |
Tensile Strength | 705 MPa (102 ksi) | 680 MPa (101 ksi) |
Yield Strength | 640 MPa (93 ksi) | 598 MPa (86 ksi) |
Elongation | 23 % | 27 % |
Current | TTW Dist. | Voltage | Wire Diameter | Wire Feed Speed |
75% Ar - 25% CO2 | ||||
130-200 A | 9.5-12.7 mm (3/8-1/2 in.) | 22-26 V | 1.2 mm (.045 in.) | 381-660 cm/min (150-260 in./min) |
200-225 A | 12.7-19 mm (1/2-3/4 in.) | 24-27 V | 1.2 mm (.045 in.) | 660-965 cm/min (260-380 in./min) |
225-265 A | 19-25.4 mm (3/4-1 in.) | 27-29 V | 1.2 mm (.045 in.) | 965-1321 cm/min (380-520 in./min) |
135-250 A | 12.7-16 mm (1/2-5/8 in.) | 22-26 V | 1.4 mm (.052 in.) | 279-584 cm/min (110-230 in./min) |
250-295 A | 16-19 mm (5/8-3/4 in.) | 25-29 V | 1.4 mm (.052 in.) | 584-864 cm/min (230-340 in./min) |
295-355 A | 19-25.4 mm (3/4-1 in.) | 27-31 V | 1.4 mm (.052 in.) | 864-1194 cm/min (340-470 in./min) |
185-285 A | 16-19 mm (5/8-3/4 in.) | 24-28 V | 1.6 mm (1/16 in.) | 279-508 cm/min (110-200 in./min) |
285-340 A | 19-25.4 mm (3/4-1 in.) | 27-30 V | 1.6 mm (1/16 in.) | 508-762 cm/min (200-300 in./min) |
340-400 A | 25.4-31.75 mm (1-1.25 in.) | 28-32 V | 1.6 mm (1/16 in.) | 762-1067 cm/min (300-420 in./min) |
Current | Deposition Rate | Deposition Type | Diameter | Deposition Efficiency (%) | TTW Dist. | Voltage | Wire Feed Speed |
150 A | 1.9 kg/h (4.2 lb/h) | 1.2 mm (.045 in.) | 86 % | 28 V | 508 cm/min (200 in./min) | ||
210 A | 2.8 kg/h (6.3 lb/h) | 1.2 mm (.045 in.) | 86 % | 29 V | 762 cm/min (300 in./min) | ||
250 A | 3.9 kg/h (8.5 lb/h) | 1.2 mm (.045 in.) | 87 % | 30 V | 1016 cm/min (400 in./min) | ||
290 A | 4.8 kg/h (10.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 33 V | 1270 cm/min (500 in./min) | ||
155 A | 2.0 kg/h (4.4 lb/h) | 1.4 mm (.052 in.) | 87 % | 25 V | 381 cm/min (150 in./min) | ||
245 A | 3.3 kg/h (7.3 lb/h) | 1.4 mm (.052 in.) | 86 % | 28 V | 635 cm/min (250 in./min) | ||
310 A | 4.6 kg/h (10.2 lb/h) | 1.4 mm (.052 in.) | 85 % | 33 V | 889 cm/min (350 in./min) | ||
360 A | 6.0 kg/h (13.3 lb/h) | 1.4 mm (.052 in.) | 85 % | 36 V | 1143 cm/min (450 in./min) | ||
190 A | 2.8 kg/h (6.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 27 V | 38 cm/min (150 in./min) | ||
300 A | 4.6 kg/h (10.2 lb/h) | 1.6 mm (1/16 in.) | 87 % | 30 V | 35 cm/min (250 in./min) | ||
365 A | 5.6 kg/h (12.3 lb/h) | 1.6 mm (1/16 in.) | 86 % | 33 V | 762 cm/min (300 in./min) | ||
410 A | 6.4 kg/h (14.0 lb/h) | 1.6 mm (1/16 in.) | 88 % | 33 V | 889 cm/min (350 in./min) | ||
75% Ar - 25% CO2 | |||||||
130-200 A | Full Range | 1.2 mm (.045 in.) | 9.5-12.7 mm (3/8-1/2 in.) | 22-26 V | 381-660 cm/min (150-260 in./min) | ||
200-225 A | Full Range | 1.2 mm (.045 in.) | 12.7-19 mm (1/2-3/4 in.) | 24-27 V | 660-965 cm/min (260-380 in./min) | ||
225-265 A | Full Range | 1.2 mm (.045 in.) | 19-25.4 mm (3/4-1 in.) | 27-29 V | 965-1321 cm/min (380-520 in./min) | ||
135-250 A | Full Range | 1.4 mm (.052 in.) | 12.7-16 mm (1/2-5/8 in.) | 22-26 V | 279-584 cm/min (110-230 in./min) | ||
250-295 A | Full Range | 1.4 mm (.052 in.) | 16-19 mm (5/8-3/4 in.) | 25-29 V | 584-864 cm/min (230-340 in./min) | ||
295-355 A | Full Range | 1.4 mm (.052 in.) | 19-25.4 mm (3/4-1 in.) | 27-31 V | 864-1194 cm/min (340-470 in./min) | ||
185-285 A | Full Range | 1.6 mm (1/16 in.) | 16-19 mm (5/8-3/4 in.) | 24-28 V | 279-508 cm/min (110-200 in./min) | ||
285-340 A | Full Range | 1.6 mm (1/16 in.) | 19-25.4 mm (3/4-1 in.) | 27-30 V | 508-762 cm/min (200-300 in./min) | ||
340-400 A | Full Range | 1.6 mm (1/16 in.) | 25.4-31.75 mm (1-1.25 in.) | 28-32 V | 762-1067 cm/min (300-420 in./min) |
Classifications | ASME SFA 5.36 :ASME SFA 5.29 :AWS A5.36 : E91T-M21A6-K2H4AWS A5.29 : E91T1-GM-H4 |
Approvals | ABSQPL-24403/2 MIL-101TM |
Approvals are based on factory location. Please contact ESAB for more information. |
Typical Weld Metal Analysis % | ||||||||||||||
C | Mn | Ni | P | S | Si | |||||||||
75% Ar - 25% CO2 | ||||||||||||||
0.059 % | 1.37 % | 2.09 % | 0.012 % | 0.010 % | 0.36 % |
搜好货厂家赫克托(上海)焊材有限公司为您提供瑞典伊萨DUAL SHIELD II 80-NI1H4低合金钢药芯焊丝的详细产品价格、产品图片等产品介绍信息,您可以直接联系厂家获取瑞典伊萨DUAL SHIELD II 80-NI1H4低合金钢药芯焊丝的具体资料,联系时请说明是在搜好货网看到的。
品牌 : | 伊萨 |
型号 : | SHIELD II 80-NI1H4 |
产地 : | 瑞典 |
类型 : | 药芯 |
材质 : | 合金 |
助焊剂含量 : | 1 |
加工定制 : | 否 |
焊丝直径 : | 1.2-1.6 |
熔点 : | 120 |
长度 : | 盘装 |
重量 : | 15公斤/盘 |
工作温度 : | 80-120 |
焊接电流 : | 180 |
是否含助焊剂 : | 否 |
适用范围 : | 广泛 |
联 系 人
联系电话
采购说明