Dual Shield B6 is an all-position flux cored electrode designed for using with 75% Ar / 25% CO2 or 100% CO2 shielding gas. Dual Shield B6 is intended for use on pipe and plate steels having a nominal 5% chromium - 0.5% molybdenum composition. These steels are typically used in process piping in the oil, gas, petrochemical, and marine industries.
Condition | Stress Relieved | Stress Relieved |
Shielding Gas | 75% Ar - 25% CO2 | 100% CO2 |
Tensile Strength | 676 MPa (98 ksi) | 640 MPa (93 ksi) |
Yield Strength | 580 MPa (84 ksi) | 540 MPa (78 ksi) |
Elongation | 20 % | 20 % |
Testing Time | 2 hr | 2 hr |
Testing Temperature | 746 degC (1375 degF) | 746 degC (1375 degF) |
Current | Deposition Rate | Diameter | Deposition Efficiency (%) | Voltage | Wire Feed Speed |
75% Ar - 25% CO2 | |||||
150 A | 1.91 kg/h (4.2 lb/h) | 1.2 mm (.045 in.) | 86 % | 28 V | 508 cm/min (200 in./min) |
210 A | 86 kg/h (6.3 lb/h) | 1.2 mm (.045 in.) | 86 % | 29 V | 762 cm/min (300 in./min) |
250 A | 3.86 kg/h (8.5 lb/h) | 1.2 mm (.045 in.) | 87 % | 30 V | 1016 cm/min (400 in./min) |
290 A | 4.85 kg/h (10.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 33 V | 1270 cm/min (500 in./min) |
330 A | 5.76 kg/h (12.7 lb/h) | 1.2 mm (.045 in.) | 87 % | 34 V | 1524 cm/min (600 in./min) |
155 A | 2 kg/h (4.4 lb/h) | 1.4 mm (.052 in.) | 87 % | 25 V | 381 cm/min (150 in./min) |
245 A | 3.31 kg/h (7.3 lb/h) | 1.4 mm (.052 in.) | 86 % | 28 V | 635 cm/min (250 in./min) |
310 A | 4.63 kg/h (10.2 lb/h) | 1.4 mm (.052 in.) | 85 % | 33 V | 889 cm/min (350 in./min) |
360 A | 6.03 kg/h (13.3 lb/h) | 1.4 mm (.052 in.) | 85 % | 36 V | 1143 cm/min (450 in./min) |
430 A | 7.98 kg/h (17.6 lb/h) | 1.4 mm (.052 in.) | 87 % | 37 V | 1524 cm/min (600 in./min) |
190 A | 2.77 kg/h (6.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 27 V | 38 cm/min (150 in./min) |
300 A | 4.63 kg/h (10.2 lb/h) | 1.6 mm (1/16 in.) | 87 % | 30 V | 35 cm/min (250 in./min) |
365 A | 5.58 kg/h (12.3 lb/h) | 1.6 mm (1/16 in.) | 86 % | 33 V | 762 cm/min (300 in./min) |
410 A | 6.35 kg/h (14 lb/h) | 1.6 mm (1/16 in.) | 88 % | 33 V | 889 cm/min (350 in./min) |
450 A | 7.3 kg/h (16 lb/h) | 1.6 mm (1/16 in.) | 87 % | 33 V | 1016 cm/min (400 in./min) |
500 A | 9.11 kg/h (20.1 lb/h) | 1.6 mm (1/16 in.) | 87 % | 39 V | 1270 cm/min (500 in./min) |
Classifications | ASME SFA 5.36 :ASME SFA 5.29 :AWS A5.36 : E81T1-C1PZ-B6AWS A5.36 : E81T1-M21PZ-B6AWS A5.29 : E81T1-B6C/E81T1-B6M |
Typical Weld Metal Analysis % | ||||||||||||||
C | Cr | Mn | Mo | P | S | Si | ||||||||
100% CO2 | ||||||||||||||
0.08 % | 4.70 % | 0.60 % | 0.50 % | 0.01 % | 0.006 % | 0.50 % | ||||||||
75% Ar - 25% CO2 | ||||||||||||||
0.05 % | 5.40 % | 0.50 % | 0.50 % | 0.006 % | 0.007 % | 0.70 % |
搜好货厂家赫克托(上海)焊材有限公司为您提供瑞典伊萨DUAL SHIELD B6低合金钢药芯气保焊丝的详细产品价格、产品图片等产品介绍信息,您可以直接联系厂家获取瑞典伊萨DUAL SHIELD B6低合金钢药芯气保焊丝的具体资料,联系时请说明是在搜好货网看到的。
品牌 : | 伊萨 |
型号 : | DUAL SHIELD B6 |
产地 : | 瑞典 |
类型 : | 药芯 |
材质 : | 合金 |
助焊剂含量 : | 1 |
加工定制 : | 否 |
焊丝直径 : | 1.2-1.6 |
熔点 : | 120 |
长度 : | 盘装 |
重量 : | 15公斤/盘 |
工作温度 : | 80-120 |
焊接电流 : | 120 |
是否含助焊剂 : | 否 |
适用范围 : | 广泛 |
联 系 人
联系电话
采购说明